Viktor Udachin

Non-thermal plasma deoxidation of copper and iron surfaces: process efficiency and mechanisms


voorkant	achterkant

ISBN:

978-3-8440-9623-1

Reeks:

Fortschrittsberichte der Materialforschung und Werkstofftechnik / Bulletin of Materials Research and Engineering
Uitgever: Clausthaler Zentrum für Materialtechnik
Clausthal

Volume:

Trefwoorden:

Plasma; Physics; Deoxidation; Copper; Iron; Oxygen-free

Soort publicatie:

Dissertatie

Taal:

Engels

Pagina's:

198 pagina's

Gewicht:

264 g

Formaat:

21 x 14,8 cm

Bindung:

Softcover

Prijs:

58,80 € / 73,60 SFr

Verschijningsdatum:

September 2024

Kopen:

Download:

Beschikbare online documenten voor deze titel:

U heeft Adobe Reader, nodig, om deze bestanden te kunnen bekijken. Hier vindt u ondersteuning en informatie, bij het downloaden van PDF-bestanden.

Let u er a.u.b. op dat de online-bestanden niet drukbaar zijn.


	Document		Samenvatting
	Soort bestand		PDF
	Kosten		gratis
	Acties		Het bestand tonen - 61 kB (62778 Byte)
	Acties		downloaden van het bestand - 61 kB (62778 Byte)


	Document		Document
	Soort bestand		PDF
	Kosten		44,10 EUR
	Acties		Tonen en kopen van het bestand - 8,1 MB (8461034 Byte)
	Acties		Kopen en downloaden van het bestand - 8,1 MB (8461034 Byte)


	Document		Inhoudsopgave
	Soort bestand		PDF
	Kosten		gratis
	Acties		Het bestand tonen - 209 kB (213618 Byte)
	Acties		downloaden van het bestand - 209 kB (213618 Byte)

Gebruikersinstellingen voor geregistreerde online-bezoekers

Hier kunt u uw adresgegevens aanpassen en uw documenten inzien.

Gebruiker:	niet aangemeld
Acties:	aanmelden/registreren Paswoord vergeten?

Aanbevelen:

Wilt u dit boek aanbevelen?

Recensie-exemplaar

Bestelling van een recensie-exemplaar.

Verlinking

Wilt u een link hebben van uw publicatie met onze online catalogus? Klik hier.

Samenvatting

The use of metals is of great importance for social progress. However, native oxide layers on metal surfaces, typically formed in the ambient atmosphere, often have a negative influence on the properties and performance of materials in metal joining operations. Thus, the reduction of oxide layers, referred to as surface deoxidation, is an important part of current research efforts, and its successful implementation could offer a range of benefits to the metalworking industry.
Conventional methods of deoxidation, such as chemical treatment or grinding, while partially effective, pose challenges due to potential alteration of surface properties. In contrast, the use of non-thermal plasmas in hydrogen-containing atmospheres represents a promising alternative.
In particular, dielectric barrier discharge (DBD) appears to be one of the most advantageous candidates, as it is effective at atmospheric pressure and has a relatively simple design that can be scaled up to industrial applications. Nevertheless, despite the high potential of the method, the deoxidation effect and mechanisms of the process on various metal surfaces have not been properly investigated.
The work reveals the efficiency and possible mechanisms of deoxidation of copper and iron oxidized surfaces in a non-thermal DBD plasma. The effect of a DBD plasma was examined at 1000 hPa in different atmospheres such as industry-relevant Ar and Ar/H2 as well as promising oxygen-free Ar/SiH4. By varying the operating parameters of the process, such as treatment time and surface temperature, the optimal conditions for the complete reduction of copper and iron surface oxides were identified. As a result, a possible model for surface oxide reduction under DBD plasma in hydrogen-containing gases was proposed.