Thomas Schneiders

Evaluation and Method Development to Improve the Adhesion of Electrospun Fibres on Metals for Use in Medical Applications


voorkant	achterkant

ISBN:

978-3-8440-9227-1

Reeks:

Textiltechnik/Textile Technology
Uitgever: Univ.-Prof. Professor h. c. (MGU) Dr.-Ing. Dipl.-Wirt. Ing. Thomas Gries
Aachen

Trefwoorden:

Textile technology; ultrafine fibres; nanofibres; stents; stent coating; adhesion; peel test

Soort publicatie:

Dissertatie

Taal:

Engels

Pagina's:

228 pagina's

Gewicht:

339 g

Formaat:

21 x 14,8 cm

Bindung:

Softcover

Prijs:

49,80 € / 62,30 SFr

Verschijningsdatum:

September 2023

Kopen:

Download:

Beschikbare online documenten voor deze titel:

U heeft Adobe Reader, nodig, om deze bestanden te kunnen bekijken. Hier vindt u ondersteuning en informatie, bij het downloaden van PDF-bestanden.

Let u er a.u.b. op dat de online-bestanden niet drukbaar zijn.


	Document		Document
	Soort bestand		PDF
	Kosten		37,35 EUR
	Acties		Tonen en kopen van het bestand - 6,8 MB (7158524 Byte)
	Acties		Kopen en downloaden van het bestand - 6,8 MB (7158524 Byte)


	Document		Inhoudsopgave
	Soort bestand		PDF
	Kosten		gratis
	Acties		Het bestand tonen - 436 kB (446070 Byte)
	Acties		downloaden van het bestand - 436 kB (446070 Byte)

Gebruikersinstellingen voor geregistreerde online-bezoekers

Hier kunt u uw adresgegevens aanpassen en uw documenten inzien.

Gebruiker:	niet aangemeld
Acties:	aanmelden/registreren Paswoord vergeten?

Aanbevelen:

Wilt u dit boek aanbevelen?

Recensie-exemplaar

Bestelling van een recensie-exemplaar.

Verlinking

Wilt u een link hebben van uw publicatie met onze online catalogus? Klik hier.

Samenvatting

The aim of this work is to develop an understanding of the adhesion mechanisms between ultrafine fibres and metallic substrates and a method for improving the adhesion at the interface. Electrospinning is used for producing ultrafine fibres, and peel force and resistance, according to DIN EN 29073-3, are used to evaluate the adhesion. Braided stents from nitinol are selected as a medical device, and thermoplastic polyurethane (TPU) for the ultrafine fibres. The stent structure is abstracted into a flat braid and a plate to investigate the influence of parameters such as effective width, surface struc-ture, or wraparound of fibres on adhesion. A fixture for peel tests on cylindrical structures is developed, and the corresponding test method is validated.
Pre-coating of stent structures leads to the highest peel resistance of 642 ± 120 cN/cm and is assessed as a suitable bonding method for producing ultrafine fibre-coated stents. The evaluation shows that interdiffusion is the best practice to increase adhesion, followed by increasing covalent bonds. The wrap-around of ultrafine fibres around stent struts exerts the greatest influence on adhesion. As validation of the results, pre-coated pulmonary stents are pre-coated with an ultrafine fibre coating, are crimped, placed into a catheter and deployed. No delamination or damaging of the interface or fibre coating occurred during the validation tests. Finally, the potential of the technology is evaluated in a business case regarding the development in publicly funded projects and the exploitation of a start-up company called StentCoat GmbH.